耐候(hou)鋼(gang)牌號及耐候鋼化學成分
耐候鋼牌號
常見的耐候鋼牌號有：Q235NQR1、Q295NQR1、Q295NQR2、Q355NQR1、Q355NQR2、Q415NQR1、Q460NQR1、Q500NQR1、Q550NQR1、Q265NQL2、Q310NQL2、Q245NYR1、Q325NYR1。
耐候鋼化學成分表
| 耐候鋼牌號 | 質量等級 | C | Si | Mn | P | S | Cu | Cr | Ni | 其他元素 |
| Q235NQR1 | C、D、E | ≤0.13 | 0.10~0.40 | 0.20~0.60 | ≤0.030 |
≤0.030 ≤0.020 ≤0.010 |
0.25~0.55 | 0.40~0.80 | ≤0.65 | a，b |
| Q295NQR1 | C、D、E | ≤0.15 | 0.10~0.50 | 0.60~1.00 | ≤0.030 |
≤0.030 ≤0.020 ≤0.010 |
0.25~0.55 | 0.40~0.80 | ≤0.65 | a，b |
| Q295NQR2 | C、D | ≤0.12 | 0.10~0.40 | 0.20~0.50 | 0.07~0.12 |
≤0.030 ≤0.020 |
0.25~0.45 | 0.30~0.65 | ≤0.50 | a，b |
| Q355NQR1 | C、D、E | ≤0.16 | ≤0.50 | 0.50~1.50 | ≤0.030 |
≤0.030 ≤0.020 ≤0.010 |
0.25~0.55 | 0.40~0.80 | ≤0.65 | a，b |
| Q355NQR2 | C、D | ≤0.12 | 0.20~0.75 | ≤1.00 | 0.07~0.15 |
≤0.030 ≤0.020 |
0.25~0.55 | 0.30~1.25 | ≤0.65 | a，b |
| Q415NQR1 | E | ≤0.12 | ≤0.65 | ≤1.10 | ≤0.025 |
≤0.010 |
0.25~0.55 | 0.30~1.25 | 0.12~0.65 | a，c |
| Q460NQR1 | E | ≤0.12 | ≤0.65 | ≤1.40 | ≤0.025 |
≤0.010 |
0.25~0.55 | 0.30~1.25 | 0.12~0.65 | a，c |
| Q500NQR1 | E | ≤0.12 | ≤0.65 | ≤2.0 | ≤0.025 |
≤0.010 |
0.25~0.55 | 0.30~1.25 | 0.12~0.65 | a，c |
| Q550NQR1 | E | ≤0.16 | ≤0.65 | ≤2.0 | ≤0.025 |
≤0.010 |
0.25~0.55 | 0.30~1.25 | 0.12~0.65 | a，c |
| Q265NQL2 | — | ≤0.12 | 0.10~0.40 | 0.20~0.50 | 0.07~0.12 |
≤0.030 |
0.25~0.45 | 0.30~0.65 | 0.25~0.50 |
a，b |
| Q310NQL2 | — | ≤0.12 | 0.25~0.75 | 0.20~0.50 | 0.07~0.12 |
≤0.030 |
0.25~0.50 | 0.30~1.25 | ≤0.65 |
a，b |
| Q245NYR1 | — | ≤0.14 | ≤0.55 | ≤1.50 | ≤0.030 |
≤0.030 |
0.15~0.40 | 0.80~1.30 | M：≤0.30 | |
| Q325NYR1 | — | ≤0.14 | ≤0.55 | ≤1.50 | ≤0.030 | ≤0.030 | — | 0.80~1.30 | — | Nb：≤0.10 |
a 可以在耐候鋼中添加添加一種或一種以上的微量合金元素，如：Nb 0.015％～0.060％，V 0.02％～0.12％，Ti 0.02％～0.10％， Alt ≥0.020％；來加強改善耐候鋼的性能。
b 可以添加：Mo≤0.30％，Zr≤0.15％合金元素。
c Nb、V、Ti等合金元素的添加總量不應超過 0.15％。
耐候鋼 成品鋼材化學成分的允許偏差應符合 GB/T 222 的規定。
耐候鋼冶煉方法
耐候鋼由轉爐或電爐冶煉，且為鎮靜鋼。除非需方有特殊要求,冶煉方法由供方選擇